How to use silicon calcium wire correctly to ensure the process effect!

Mar 04, 2020 / 1062 views


Many  types  of  additives  are  added  to  the  smelting  of  steel.  For  different  additives,  the  effects  they  play  are  different.  Silicon-calcium  wire  is  a  common  additive  in  our  lives.  Other  additives  are  different.  Only  in  the  correct  way  of  adding  ferroalloy  can  the  function  of  silicon  calcium  wire  be  better  played.  So  how  to  use  silicon  calcium  wire  correctly?  Let's  follow  the  manufacturers  of  silicon  calcium  wire  to  find  out.

Solid  core  pure  calcium  wire  reacts  with  molten  steel  more  fiercely  than  silicon  calcium  wire  during  calcium  treatment.  Caution  should  be  paid  to  the  calcium  treatment  operations,  such  as  feeding  depth  and  wire  feeding  speed.  Due  to  the  high  vapor  pressure  of  the  solid  core  pure  calcium  wire,  In  order  to  prevent  the  natural  evaporation  of  calcium,  solid  pure  calcium  wire  must  be  fed  deep.  One  method  is  to  increase  the  thickness  of  the  iron  sheet  to  prevent  its  premature  melting  from  affecting  the  depth  of  calcium  release.  The  other  method  is  to  increase  the  wire  feeding  speed  to  increase  the  calcium.  Depth  of  release,  high  wire  feed  speed  enables  solid  core  pure  calcium  wire  to  penetrate  the  slag  layer  and  reach  a  certain  depth,  reducing  the  oxidation  of  Ca  by  slag,  increasing  the  absorption  of  calcium  by  molten  steel,  and  improving  the  recovery  rate  of  calcium.

Feeding  line  speed  and  feeding  rhythm  are  the  key  parameters  of  solid  core  pure  calcium  line  feeding  process.  Too  fast  or  slow  feeding  speed  will  affect  the  melting  time  and  oxidation  degree  of  solid  core  pure  calcium  line,  which  will  affect  the  metallurgical  effect.  The  operator  must  pay  close  attention  to  the  molten  steel  situation.  Once  the  molten  steel  tumbles  fiercely,  he  must  pause  for  a  while  before  continuing  to  feed  the  wire  to  prevent  splashing.


Hot Visit on FerroEast.com: Ferroalloys Conference Ferrosilicon Silicon Metal High Carbon Ferro Silicon Silicon Briquette FerroSilicon Briquette Ferromanganese Silicon Manganese Graphite Powder Petroleum Coke Calcium Silicon Calcium Silicon Cored Wire Silicon Slag Silicon Carbide Silicon Barium Electrolytic Manganese Metal Flakes Ferro silicon Ferro Manganese